By the way....
Speaking of annealing - I used to anneal after each firing. I stopped doing it that often & only anneal after 2 to 3 firings. I notice a better consistancy with the tighter neck fit. I'm wondering if maybe I wasn't making the brass necks a little too soft.

The most noticeable difference is in how much pressure is needed to seat the bullets. Now that you can anneal brass to death, you may want to consider that frequency you cook your cases.

Do you shoot competition? How often do you heat treat? What kind of consistancy do you notice?

Off to hit the proverbial rack. Busy day tomorrow.

Later y'all

Frank in fla