Forgive me if I'm over thinking this but as a former aviation guy I'm fairly familiar with the problems caused by dissimilar metals mating up to each other. I'm about to start into my 3rd Savage Re-barrel/build and found a really good deal on a SS barrel but not sure if I will have corrosion issues down the road because it's a chrome-molly blued receiver. Any insight would be great?

BTW I did find this thread http://www.savageshooters.com/archiv...p/t-34127.html however it seems to be more "yeah it looks cool and shoots fine" than actually address the dissimilar metal + heat + time = corrosion? issue.