Also, I forgot to ask what condition it would be treated to?
Does anyone know what Stainless alloy the PTA is made of? 416, 17-4PH, 15.5PH or other?
If you know I'd like to know too.
Thanks!
Also, I forgot to ask what condition it would be treated to?
416 SS vacuum furnace heat treat to 38-42 Rc.
"As long as there's lead in the air....there's still hope.."
Fred,
When I posted that I felt you would be the one that knows. Thanks for your reply!
Phil